China wholesale 5086 h116 aluminum sheet factory prices
Author：Mingtai aluminum
View：
Time：2020-05-07
China wholesale 5086 h116 aluminum sheet factory prices
china 5086 aluminum sheet factory supply h116 aluminum sheet prices
Mingtai Aluminu is a renowned public China wholesale 5086 h116 aluminum plate factory. China wholesale 5086 h116 aluminum sheet factory prices , Presently, the company’s products cover aluminum alloy products of Series 1xxx, Series 3xxx, Series 4xxx, Series 5xxx, Series 6xxx, Series 7xxx, Series 8xxx of different sizes. Main products include various alloy of aluminum plate, strip, foil, aluminum coil, aluminum embossed sheet, diamond aluminum plate. Those products are widely applied in industries including automobile making, traffic and transportation, packaging and containers, buildings and decorations, electrical and electronic, printing, etc
the Al-Mg alloy and Al-Mn alloy both are anti-rust aluminum alloy components, it increase their anti-corrosion properties, Al-Mn alloy is 3003,3004,3105, Al-Mg alloy were 5005,5252,5251,5050 5052,5754,5083,5056 ,5086 aluminum sheet, according to the level of the Mg content
1. high corrosion resistance, medium strength, good weld-ability;
2. low density, high tensile strength, high elongation
3. with no oil, no waves, no scratches, no roller, uniform cutting edges and burr
5086 is the preferred hull material for small aluminium boats or larger yachts. Its high strength and good corrosion resistance make it an excellent match for yachting.
5086 has a tendency to undergo Stress corrosion cracking and is not used much in aircraft construction as a result.
5086 has been used in vehicle armor, notably in the M113 Armored Personnel Carrier and M2 Bradley Infantry fighting vehicle.
Welding of China wholesale 5086 h116 aluminum sheet
5086 is often assembled using arc welding, typically MIG or TIG welding. The newer technique of Friction stir welding has also been successfully applied but is not in common use.
Arc welding reduces mechanical properties to no worse than –O hardening condition. For –H116 base material, measured at 20 °C (68 °F) ambient temperature, yield strength decreases from 210 MPa (30 ksi) to 120 MPa (17 ksi) and ultimate strength from 290 to 260 MPa (42 to 38 ksi). The relatively low decrease in ultimate strength (about 10%) is extremely good performance for an aluminium alloy.